High quality window brushes are used for their ability to spread adequate water without scratching the glass. They help prevent sand from getting trapped between the brush and the glass. Strip washers are also commonly used, but hold less water and carry a higher risk of trapping construction debris, which can scratch glass more easily.
Yes. Steel wool is sometimes used to remove construction debris from glass, but carries a higher risk of scratching glass. If construction debris gets trapped between the steel wool and glass, scratching could result. Also, if steel wool is to be used, use only new steel wool. If rust is present in old steel wool, scratched glass will result.
Usually just called tempered glass, fully tempered glass is a safety glass used in many applications where the possibility of human contact is high. This glass is 4-5 times stronger than non-tempered glass and breaks into very small pieces when fractured.
Heat strengthened glass is twice as strong as non-tempered glass. Fracture characteristics of heat strengthened glass vary widely from much like annealed glass to similar to fully tempered glass. For this reason, heat strengthened glass does not qualify as a safety glass.
Laminated glass consists of two or more panes of glass with a tough plastic interlayer, bonded together under heat and pressure. Laminated glass is also used as an effective sound control product. Laminated glass is commonly used in airports, sound studios, schools and in houses near freeways to keep away unwanted noise from airplanes, heavy machinery and traffic.
Anywhere glass is more prone to human contact such as doors, windows close to the floor, stair landings and tub/shower enclosures. Check your local building code for details or more specific locations.
Tempered glass must first be cut to the finished size, since it cannot be cut or modified after it is tempered. Then the edges are belt seamed or sanded to remove any sharp edges. Next it is washed to remove all fabricating debris. Finally, it is heated to almost 1200°F and then quick cooled, which produces the temper.